Synthesis and Characterization of Epoxy Resins-Modified Waterborne Polyurethane Emulsion
Asian Journal of Applied Chemistry Research,
Aqueous polyurethane emulsion was prepared with diphenylmethane diisocyanate (MDI), polybutylene adipate diol (PBA-1000) as main raw materials and 2, 2-dihydroxymethyl propionic acid (DMPA) as hydrophilic chain extender. On this basis, epoxy resin E-44 was introduced to modify the polyurethane prepolymer, and epoxy resin modified waterborne polyurethane emulsion was obtained. In order to obtain better performance waterborne polyurethane, the effect of DMPA content、the amount of epoxy resin added and modification method on the properties of polyurethane was discussed. The results show that when the DMPA content is 4wt%, the overall performance of the emulsion and the film is the best. And the addition of epoxy resin significantly improves the water resistance, solvent resistance and tensile strength of the waterborne polyurethane film, and its hardness and thermal stability are also improved to a certain extent. When the amount of epoxy resin added is 8wt%, the storage stability decreases significantly, the suitable amount of epoxy resin added is 6wt%. The overall performance of the film obtained by chemical modification is better than that of physical modification.
- Waterborne polyurethane
- epoxy resin
How to Cite
Liu H, Song J, Shang S, et al. Cellulose nanocrystal/silver nanoparticle composites as bifunctional nanofillers within waterborne polyurethane[J]. ACS Appl. Mater. Inter. 2012;4(5): 2413-2419.
LI P X, LIU C X, YU X Y, et al. Study on Preparation and Performance of Epoxy Resin Modified Waterborne Polyurethane Coating ［J］．Colloids and Polymers. 2020;38(03)．
GUO H Y, LIU Y, DENG Y J. Study on Preparation and Performance of Epoxy Resin Modified Waterborne Polyurethane[J]. Polyurethane Industry. 2019;34(01).
Epstein BN, Del W. Tough thermoplastic nylon composition [P]. U.S. Patent: 4174358, 1979;11:13.
Miller JA, Huang KKS, Cooper SL. Properties of Polyether–Polyurethane Anionomers. J Macromol Sci. 1983;B22:321.
CHEN B, DENG Y, CHEN S, et al. Research Progress of Waterborne Polyurethane Modification [J]. Textile Science Research. 2018;(01).
Chattopadhyay DK, Raju K. Structural engineering of polyurethane coatings for high performance applications [J]. Progress in Polymer Science. 2007;32(3):352-418.
QU J Q，LUO C H，CHEN H Q．Crosslinking modificationand film properties of waterborne polyurethane -acrylate［J］．Journal of South China University of Technology( Natural Science Edition) ，2009;37( 6):53 -57．
AHMAD S，GUPTA A P，SHARMIN E，et al． Synthesis，characterization and development of high performance silox-ane- modified epoxy paints［J］． Progress in Organic Coat-ing. 2005;54(3):248 - 255．
Yao K J, Song M, Hourston D J. Polymer/layeredclay nanocomposites Polyurethane composites [J]. Polymer. 2002;43:1435-1543.
B.K. Kim, B.U. Ahn, M.H. Lee, S.K. Lee. Design and properties of UV cured polyurethane dispersions [J]. Progress in Organic Coatings, 2005;55(2).
Zhang M, Song F, Wang X et al. Development of soy protein isolate/waterborne polyurethane blend films with improved properties [J]. Colloid Surface B. 2012;100:16-21.
ZHENG Y,HU P.ZHANG X, et al. Synthesis and Factor Analysis of Epoxy Modified Waterborne Polyurethane [J]. Functional Materials, 2018;49(10).
ZHOU Y Y，WANG P H，LIU C H，et al Preparation ofdiethanolamine modified waterborne epoxy resin［J］．Paint＆Coatings Industry. 2011;41(1):48-51．
WU X Q，WEI X L，QIU S J．The study on synthesistechnology and properties of water-borne polyurethane mod-ified by epoxy resin［J］．Journal of Basic Science and En-gineering. 2006;14( 2):153-159．
 ZHAN B．Preparation and study of waterborne polyurethane emulsion modified by epoxy resin ［D］．Yan Shan University. 2012;12
 Marlina , Iqhrammullah M ,Saleha, S et al. Polyurethane film prepared from ball-milled algal polyol particle and activated carbon filler for NH3-N removal. [J]. Heliyon 2020;6(8):e04590.
 Iqhrammullah M, Marlina M ,Khalil H , et al . Characterization and Performance Evaluation of Cellulose Acetate-Polyurethane Film for Lead II Ion Removal. [J] Polymers 2020;12(6):1317.
 DENG Z X,YE D Y,LI Y J, et al．Analysis and characterization of epoxy modified waterborne polyurethane [J].Insulation materials. 2007;40 (2):14- 20.
 LI L K.Preparation and properties of waterborne polyurethane modified by epoxy resin [J].Polyurethane industry. 2010;25(1):42-45.
Abstract View: 67 times
PDF Download: 16 times